| Area of Application |
Brand |
Al2O3
(%) |
Fe2O3
(%) |
A.P.
(%) |
B.D. (gms/cc) |
CCS (kgs
/cm2) |
PCE (OC) |
RUL (Ta) |
PLC (%)
(℃/Hrs) |
| |
|
Min. |
Max. |
Min. |
Min. |
Min℃ |
|
|
|
| Preheated Cyclones |
SVRL
3035 |
30 |
3.5 |
21/24 |
2.10 |
250/
350 |
30 |
- |
- |
| Preheated Cyclones
Inlet Housing, Cooler Walls |
SVRL
4030 |
40 |
3.0 |
20/22 |
2.20 |
350 |
31/32 |
- |
- |
| Pre Calcinator |
SVRL
4515 |
45 |
1.5 |
16/20 |
2.25 |
400 |
34 |
1470 |
1400/2
Hrs +/-0.5 |
| Pre Calcinator Poof |
SVRL
7520 |
75 |
2.0 |
16/20 |
2.70 |
500 |
38 |
1500 |
1500/2
Hrs +1.5 |
| Calcining Zone of Rotary Kiln |
SVRL
4030 |
40 |
3.0 |
22 |
2.20 |
300/
350 |
31/32 |
- |
- |
| Safety Zone of Rotary Kiln |
SVRL
6030 |
60 |
3.0 |
23 |
2.50 |
500 |
35 |
1420 |
1420/2
Hrs +1.0 |
| Upper Transition Zone If Alkali Problem Does Not Exist |
SVRL
7030 |
70 |
3.0 |
19/23 |
2.65 |
500/
700 |
36 |
1450 |
1500/2
Hrs +3.0 |
| Upper Transition Zone Where
Alkali Problem Exist. |
SVRL
LFCB
7020 |
70 |
2.0 |
13/18 |
2.70 |
600/
1000 |
37 |
1480 |
- |
| Burning Zone Lining |
SVRL
77LI |
77 |
2.0 |
21 |
2.70 |
500 |
37 |
1450 |
- |
| |
SVRL
75LI |
75 |
2.5 |
21 |
2.70 |
500 |
37 |
1450 |
- |
| |
SVRL
70LI |
70 |
2.5 |
21 |
2.65 |
500 |
36 |
1450 |
- |
| |
SVRL
7030 |
70 |
3.0 |
23 |
2.65 |
700 |
36 |
1450 |
- |
| Cooling Zone of Rotary Kiln |
SVRL
7030 |
70 |
3.0 |
19/23 |
2.65 |
500/
700 |
36 |
1450 |
- |
| Smoke Chember |
SVRL
4030 |
40 |
3.0 |
20/22 |
2.20 |
350 |
31/32 |
- |
- |
| Firing Chember |
SVRL
5030 |
50 |
3.0 |
23 |
2.35 |
350 |
32/33 |
- |
- |
| Cooler Discharble End,
Cooler Beam |
SVRL
8030S |
80 |
3.0 |
23 |
2.70 |
500 |
37 |
1400 |
1400/22 Hrs+/-1.0 |
| Tertary Air Duct. |
SVRL
3020 |
30 |
2.0 |
20 |
2.00 |
500/700 |
29 |
- |
- |
Note: Alumina When Determined May Vary Up To + 2%. |